Influence of B2O3 on Viscosity of High Ti-bearing Blast Furnace Slag

QC 20120717
The influence of B2O3 on the viscosity of high Ti-bearing BF slag is studied under Ar atmosphere from 1 773 K (1 500 degrees C) to about 1 593 K (1 320 degrees C). The results show that the addition of B2O3 can decrease the viscosity of high Ti-bearing BF Slag containing UPC, consequently improve its fluidity. With the existence of 1.5% UPC, when the content of B2O3 increased from 0 to 4.1%, the volume fraction of perovskite decreased from 7.7% to 1.6% at 1 610 K. Meanwhile, the liquidus temperatures decreased from 1 619 K to 1 613 K. At a lower temperature, B2O3 was easy to form a eutectic and decreased the viscosity of molten slag. At a higher temperature, some tetrahedron [BO4](5-) changed into triangle [BO3](3-) which would disintegrate the chains/molecules of molten matrix and decreased its viscosity.

Zhang, JianliangUniv Sci & Technol Beijing, Peoples R China (författare)
Wu, LiushunKTH,Mikro-modellering(Swepub:kth)u1z1c53o (författare)
Liu, WeijianUniv Sci & Technol Beijing, Peoples R China (författare)
Bai, YananUniv Sci & Technol Beijing, Peoples R China (författare)
Xing, XiangdongUniv Sci & Technol Beijing, Peoples R China (författare)
Su, BuxinUniv Sci & Technol Beijing, Peoples R China (författare)
Kong, DewenUniv Sci & Technol Beijing, Peoples R China (författare)
Univ Sci & Technol Beijing, Peoples R ChinaMikro-modellering (creator_code:org_t)

Ingår i:ISIJ International: Iron and Steel Institute of Japan52:6, s. 984-9910915-15591347-5460

Av författaren/redakt...: Ren, Shan; Zhang, Jianliang; Wu, Liushun; Liu, Weijian; Bai, Yanan; Xing, Xiangdong; visa fler...; Su, Buxin; Kong, Dewen; visa färre...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.