Raman Scattering and Carrier Diffusion Study in Heavily Co-doped 6H-SiC Layers

• Thick 6H-SiC epilayers were grown using the fast sublimation method on low-off-axis substrates. They were co-doped with N and B impurities of ≈1019 cm−3 and (41016–51018) cm−3 concentration, respectively. The epilayers exhibited donor-acceptor pair (DAP) photoluminescence. The micro-Raman spectroscopic study exposed a compensated n-6H-SiC epilayer of common quality with some 3C-SiC inclusions. The compensation ratio of B through 200 μm thick epilayer varied in 20-30% range. The free carrier diffusivity was studied by transient grating technique at high injection level. The determined ambipolar diffusion coefficient at RT was found to decrease from 1.15 cm2/s to virtually 0 cm2/s with boron concentration increasing by two orders.