- Bhatt, PramodLinköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan (författare)
High temperature annealing effect on structural and magnetic properties of Ti/Ni multilayer
- Artikel/kapitelEngelska2006
Förlag, utgivningsår, omfång ...
- Elsevier BV,2006
- printrdacarrier
Nummerbeteckningar
- LIBRIS-ID:oai:DiVA.org:liu-13114
- https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-13114URI
- https://doi.org/10.1016/j.apsusc.2006.05.036DOI
Kompletterande språkuppgifter
- Språk:engelska
- Sammanfattning på:engelska
Ingår i deldatabas
- SwePubSwePub
Klassifikation
Anmärkningar
- High temperature annealing effect on structural and magnetic properties of Ti/Ni multilayer (ML) up to 600 °C have been studied and reported in this paper. Ti/Ni multilayer samples having constant layer thicknesses of 50 Å each are deposited on float glass and Si(1 1 1) substrates using electron-beam evaporation technique under ultra-high vacuum (UHV) conditions at room temperatures. The micro-structural parameters and their evolution with temperature for as-deposited as well as annealed multilayer samples up to 600 °C in a step of 100 °C for 1 h are determined by using X-ray diffraction (XRD) and grazing incidence X-ray reflectivity techniques. The X-ray diffraction pattern recorded at 300 °C annealed multilayer sample shows interesting structural transformation (from crystalline to amorphous) because of the solid-state reaction (SSR) and subsequent re-crystallization at higher temperatures of annealing, particularly at ≥400 °C due to the formation of TiNi3 and Ti2Ni alloy phases. Sample quality and surface morphology are examined by using atomic force microscopy (AFM) technique for both as-deposited as well as annealed multilayer samples. In addition to this, a temperature dependent dc resistivity measurement is also used to study the structural transformation and subsequent alloy phase formation due to annealing treatment. The corresponding magnetization behavior of multilayer samples after each stage of annealing has been investigated by using Magneto-Optical Kerr Effect (MOKE) technique and results are interpreted in terms of observed micro-structural changes.
Ämnesord och genrebeteckningar
- Ti/Ni multilayer structure; Annealing effect; Interfaces properties; Magnetization measurements; Resistivity measurements
- NATURAL SCIENCES
- NATURVETENSKAP
Biuppslag (personer, institutioner, konferenser, titlar ...)
- Ganeshan, V.UGC-DAE Consortium for Scientific Research, Indore, India (författare)
- Reddy, V. R.UGC-DAE Consortium for Scientific Research, Indore, India (författare)
- Chaudhari, S. M.UGC-DAE Consortium for Scientific Research, Indore, India (författare)
- Linköpings universitetInstitutionen för teknik och naturvetenskap (creator_code:org_t)
Sammanhörande titlar
- Ingår i:Applied Surface Science: Elsevier BV253:5, s. 2572-25800169-4332
Internetlänk
Hitta via bibliotek
- Applied Surface Science (Sök värdpublikationen i LIBRIS)
Till lärosätets databas
- 1 av 1
- Föregående post
- Nästa post
- Till träfflistan
Hitta mer i SwePub
- Av författaren/redakt...
- Bhatt, Pramod
- Ganeshan, V.
- Reddy, V. R.
- Chaudhari, S. M.
- Artiklar i publikationen
- Applied Surface ...
- Av lärosätet
- Linköpings universitet
Sök utanför SwePub
- Sök vidare i:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - Nationella bibliotekssystem
- LIBRIS.kb.se