Structural evolution in reactive RF magnetron sputtered (Cr,Zr)2O3 coatings during annealing
-
- Landälv, Ludvig, 1982- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Sandvik Coromant AB, Sweden
-
- Lu, Jun, 1962- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Spitz, S. (författare)
- Karlsruhe Institute Technology, Germany
-
visa fler...
-
- Leiste, H. (författare)
- Karlsruhe Institute Technology, Germany
-
- Ulrich, S. (författare)
- Karlsruhe Institute Technology, Germany
-
- Johansson, Mats P., 1965- (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska fakulteten,Tunnfilmsfysik,SECO Tools AB, Sweden
-
- Ahlgren, M. (författare)
- Sandvik Coromant AB, Sweden
-
- Gothelid, E. (författare)
- Sandvik Coromant AB, Sweden
-
- Alling, Björn, 1980- (författare)
- Linköpings universitet,Teoretisk Fysik,Tekniska fakulteten,Max Planck Institute Eisenforsch GmbH, Germany
-
- Hultman, Lars, Professor, 1960- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
- Stueber, M. (författare)
- Karlsruhe Institute Technology, Germany
-
- Eklund, Per, Docent, 1977- (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten
-
visa färre...
-
(creator_code:org_t)
- PERGAMON-ELSEVIER SCIENCE LTD, 2017
- 2017
- Engelska.
-
Ingår i: Acta Materialia. - : PERGAMON-ELSEVIER SCIENCE LTD. - 1359-6454 .- 1873-2453. ; 131, s. 543-552
- Relaterad länk:
-
https://liu.diva-por... (primary) (Raw object)
-
visa fler...
-
http://liu.diva-port...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Reactive RF-magnetron sputtering is used to grow Cr0.28Zr0.10O0.61 coatings at 500 degrees C. Coatings are annealed at 750 degrees C, 810 degrees C, and 870 degrees C. The microstructure evolution of the pseudobinary oxide compound is characterized through high resolution state of the art HRSTEM and HREDX-maps, revealing the segregation of Cr and Zr on the nm scale. The as-deposited coating comprises cc-(Cr,Zr)(2)O-3 solid solution with a Zr-rich (Zr,Cr)O-x. amorphous phase. After annealing to 750 degrees C tetragonal ZrO2 nucleates and grows from the amorphous phase. The ZrO2 phase is stabilized in its tetragonal structure at these fairly low annealing temperatures, possibly due to the small grain size (below 30 nm). Correlated with the nucleation and growth of the tetragonal-ZrO2 phase is an increase in hardness, with a maximum hardness after annealing to 750 degrees C, followed by a decrease in hardness upon coarsening, bcc metallic Cr phase formation and loss of oxygen, during annealing to 870 degrees C. The observed phase segregation opens up future design routes for pseudobinary oxides with tunable microstructural and mechanical properties. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Nyckelord
- Chromium zirconium oxide; Eskolaite; RF magnetron sputtering; Annealing; TEM
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Landälv, Ludvig, ...
-
Lu, Jun, 1962-
-
Spitz, S.
-
Leiste, H.
-
Ulrich, S.
-
Johansson, Mats ...
-
visa fler...
-
Ahlgren, M.
-
Gothelid, E.
-
Alling, Björn, 1 ...
-
Hultman, Lars, P ...
-
Stueber, M.
-
Eklund, Per, Doc ...
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Materialkemi
- Artiklar i publikationen
-
Acta Materialia
- Av lärosätet
-
Linköpings universitet