Palmert, FransLinköpings universitet,Konstruktionsmaterial,Tekniska fakulteten,Siemens Ind Turbomachinery AB, Sweden
(författare)
Fatigue crack growth behaviour of an alternative single crystal nickel base superalloy
- Artikel/kapitelEngelska2018
Förlag, utgivningsår, omfång ...
-
ELSEVIER SCI LTD,2018
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:liu-145431
-
https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-145431URI
-
https://doi.org/10.1016/j.ijfatigue.2017.12.003DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Funding Agencies|Siemens Industrial Turbomachinery AB in Finspang, Sweden; Swedish Energy Agency, via the Research Consortium of Materials Technology for Thermal Energy Processes [KME-702]
-
The fatigue crack growth behaviour of a single crystal nickel base superalloy was studied at three different temperatures (20 degrees C, 500 degrees C and 750 degrees C) and three different crystallographic orientations. At the highest testing temperature, the influence of hold time at maximum load was also evaluated. Under some of the testing conditions, crystallographic crack growth occurred along {1 1 1} planes, which were non-perpendicular to the loading direction. The propensity for crystallographic cracking was observed to be strongly temperature dependent with a maximum occurring at the intermediate testing temperature of 500 degrees C. During non-crystallographic, Mode I crack growth the crack tended to avoid the gamma particles and propagated preferentially through the gamma matrix.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Moverare, JohanLinköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)johmo31
(författare)
-
Gustafsson, DavidSiemens Ind Turbomachinery AB, Sweden
(författare)
-
Busse, ChristianLinköpings universitet,Mekanik och hållfasthetslära,Tekniska fakulteten(Swepub:liu)chrbu94
(författare)
-
Linköpings universitetKonstruktionsmaterial