Growth and mechanical properties of 111-oriented V0.5Mo0.5Nx/Al2O3(0001) thin films

• Pseudobinary V0.5Mo0.5Nx(111) alloys with the Bl-NaCl crystal structure are grown on Al2O3(0001) substrates in an ultra-high-vacuum system by reactive magnetron sputter deposition in mixed Ar/N-2 atmospheres at temperatures T-s between 100 and 900 degrees C. Nitrogen-to-metal, N/(V + Mo), fractions x vary monotonically from 0.9 +/- 0.1 with T-s = 100 degrees C to 0.4 +/- 0.1 at T-s = 900 degrees C. Nitrogen loss at higher growth temperatures leads to a corresponding decrease in the relaxed lattice parameter a(o) from 4.21 +/- 0.01 angstrom at T-s = 300 degrees C to 4.125 +/- 0.005 angstrom with T-s = 900 degrees C. Scanning electron micrographs of cube-corner nanoindents extending into the substrate show that the films are relatively ductile, exhibiting material pile-up (plastic flow) around the indent edges. Nanoindentation hardnesses H and elastic moduli E, obtained using a calibrated Berkovich tip, of V0.5Mo0.5Nx(111) layers increase with increasing T-s(decreasing x) from 15 +/- 1 and 198 +/- 5 GPa at 100 degrees C to 23 +/- 2 and 381 +/- 11 GPa at 900 degrees C. These values are lower than the corresponding results obtained for the 001-oriented V0.5Mo0.5Nx films In addition, film wear resistance increases with increasing T-s, while the coefficient of friction, under 1000 mu N loads, is 0.09 +/- 0.01 for all layers. Published by the AVS.

Subject headings

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

Publication and Content Type

ref (subject category)

art (subject category)