Vapor phase synthesized poly(3,4-ethylenedioxy-thiophene)-trifluoromethanesulfonate as a transparent conductor material
-
- Brooke, Robert (författare)
- Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska fakulteten
-
- Franco Gonzalez, Felipe (författare)
- Linköpings universitet,Fysik och elektroteknik,Tekniska fakulteten
-
- Wijeratne, Kosala (författare)
- Linköpings universitet,Fysik och elektroteknik,Tekniska fakulteten
-
visa fler...
-
- Pavlopoulou, Eleni (författare)
- Univ Bordeaux, France
-
- Galliani, Daniela (författare)
- Univ Milano Bicocca, Italy
-
- Liu, Xianjie (författare)
- Linköpings universitet,Ytors Fysik och Kemi,Tekniska fakulteten
-
- Valiollahi Bisheh, Roudabeh (författare)
- Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska fakulteten
-
- Zozoulenko, Igor (författare)
- Linköpings universitet,Fysik och elektroteknik,Tekniska fakulteten
-
- Crispin, Xavier (författare)
- Linköpings universitet,Fysik och elektroteknik,Tekniska fakulteten
-
visa färre...
-
(creator_code:org_t)
- 2018
- 2018
- Engelska.
-
Ingår i: Journal of Materials Chemistry A. - : ROYAL SOC CHEMISTRY. - 2050-7488 .- 2050-7496. ; 6:43, s. 21304-21312
- Relaterad länk:
-
https://liu.diva-por... (primary) (Raw object)
-
visa fler...
-
https://pubs.rsc.org...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Inorganic transparent conductive oxides have dominated the market as transparent electrodes due to their high conductivity and transparency. Here, we report the fabrication and optimization of the synthesis of poly(3,4-ethylenedioxythiophene) trifluoromethanesulfonate via vapor phase polymerization for the potential replacement of such inorganic materials. The parameters and conditions of the polymerization were investigated and an electrical conductivity of 3800 S cm(-1) and 4500 S cm(-1) after acid treatment were obtained while maintaining an absorbance similar to that of commercial indium tin oxide. This increase in electrical conductivity was rationalized experimentally and theoretically to an increase in the oxidation level and a higher order of crystallinity which does not disrupt the pi-pi stacking of PEDOT chains.
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas