  • Sun, XiaoyuLinköpings universitet,Konstruktionsmaterial,Tekniska fakulteten (författare)

Revealing microstructural degradation mechanism induced by interdiffusion between Amdry365 coating and IN792 superalloy

  • Artikel/kapitelEngelska2024

Förlag, utgivningsår, omfång ...

  • ELSEVIER SCI LTD,2024
  • printrdacarrier

Nummerbeteckningar

  • LIBRIS-ID:oai:DiVA.org:liu-203640
  • https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-203640URI
  • https://doi.org/10.1016/j.matdes.2024.112937DOI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:vet swepub-contenttype
  • Ämneskategori:art swepub-publicationtype

Anmärkningar

  • Funding Agencies|Siemens Industrial Turbomachinery AB (Finspang, Sweden; Stiftelsen Axel Hultgrens Fond (Stockholm, Sweden); Swedish Government Strategic Research Area in Materials Science on Functional Materials at Link o ping University [SFO-Mat-LiU 2009- 00971]
  • Metallic coatings are widely employed to improve the oxidation resistance of superalloys. However, the interdiffusion between the metallic coatings and the superalloys leads to microstructural degradation in both. Some of the underlying degradation mechanisms are still elusive, e.g., the γ′ (Ni3Al) phase depletion in superalloys, where a large amount of γ′ precipitates are dissolved in the γ matrix even though the incoming Al from coatings indeed increases the Al content. Here, we investigated the interdiffusion behavior between the Amdry365 coating and the IN792 superalloy at 1100 °C, using multiple microscopic techniques and thermodynamics calculations. Our results showed an excellent agreement between experiments and thermodynamics simulations, indicating the dominant role of Al on the initial diffusion-induced phase transitions. We proposed the Al-Cr interference effect to account for the pile-up behavior of Cr and the reduced Al content near the coating/superalloy interface. The local phase equilibrium calculations revealed that the γ′ depletion in the superalloy is primarily attributed to the loss of γ′-forming elements, such as Ta and Ti. Our findings opened up an avenue for studies on the superalloy/coating interdiffusion, contributing to reducing this damaging impact.

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Li, XiaolongDepartment of Industrial and Materials Science, Chalmers University of Technology, Gothenburg, Sweden (författare)
  • Guo, ShengDepartment of Industrial and Materials Science, Chalmers University of Technology, Gothenburg, Sweden (författare)
  • Yu, XinInstitute for Advanced Studies in Precision Materials, Yantai University, Yantai, Shandong, China (författare)
  • Zhu, LilongInstitute for Advanced Studies in Precision Materials, Yantai University, Yantai, Shandong, China (författare)
  • Teng, JianweiInstitute for Advanced Studies in Precision Materials, Yantai University, Yantai, Shandong, China (författare)
  • Jiang, LiangInstitute for Advanced Studies in Precision Materials, Yantai University, Yantai, Shandong, China (författare)
  • Moverare, JohanLinköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)johmo31 (författare)
  • Li, Xin-HaiSiemens Energy AB, SE-61283 Finspång, Sweden (författare)
  • Peng, Ru LinLinköpings universitet,Konstruktionsmaterial,Tekniska fakulteten (författare)
  • Linköpings universitetKonstruktionsmaterial (creator_code:org_t)

Sammanhörande titlar

  • Ingår i:Materials & design: ELSEVIER SCI LTD2410264-12751873-4197

Internetlänk

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy