Oxidation behavior of Ni-based superalloy GH4738 under tensile stress

• Revealing the oxidation behavior of superalloys is crucial for optimizing material properties and extending service life. This study investigated the oxidation behavior of superalloy GH4738 under stress states at 850 degrees C. High-throughput specimens were fabricated to withstand different stresses at the same time. Isothermal oxidation samples were analyzed using the mass gain method to obtain oxidation kinetic curves. The results show that the external stress below 200 MPa could improve the oxidation resistance of the GH4738. With tensile stress increasing, the oxide layer becomes thinner, denser and more complete, while internal oxidation decreases. The tensile stress alters the structure of the external oxide layer from a two-layer to a three-layer configuration. The Cr2O3 oxide layer inhibits the outward diffusion of Ti, leading to Ti enrichment at the oxide-matrix interface and altering the oxidation mechanism of GH4738.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

Ni-based; Superalloy; Oxidation behavior; Tensile stress; Oxide layer

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)