Oxidation behavior of Ni-based superalloy GH4738 under tensile stress

Funding Agencies|Shandong Provincial Natural Science Foundation for Youths; National Key R&D Program of China [2021YFB3700401]; Zhejiang Provincial Natural Science Foundation [LQ21E030002]; Youth Innovation team Project of Higher Education Institutions in Shandong Province [2022KJ272]; [ZR2022QE234]
Revealing the oxidation behavior of superalloys is crucial for optimizing material properties and extending service life. This study investigated the oxidation behavior of superalloy GH4738 under stress states at 850 degrees C. High-throughput specimens were fabricated to withstand different stresses at the same time. Isothermal oxidation samples were analyzed using the mass gain method to obtain oxidation kinetic curves. The results show that the external stress below 200 MPa could improve the oxidation resistance of the GH4738. With tensile stress increasing, the oxide layer becomes thinner, denser and more complete, while internal oxidation decreases. The tensile stress alters the structure of the external oxide layer from a two-layer to a three-layer configuration. The Cr2O3 oxide layer inhibits the outward diffusion of Ti, leading to Ti enrichment at the oxide-matrix interface and altering the oxidation mechanism of GH4738.

Huang, Hai-LiangYantai Univ, Peoples R China (författare)
Wu, Chong-ChongYantai Univ, Peoples R China (författare)
Sun, Xiao-YuLinköpings universitet,Konstruktionsmaterial,Tekniska fakulteten(Swepub:liu)xiasu56 (författare)
Wang, JieYantai Univ, Peoples R China (författare)
Yang, Yan-HongChinese Acad Sci, Peoples R China (författare)
Qu, Jing-LongGaona Aero Mat Co Ltd, Peoples R China (författare)
Jiang, LiangYantai Univ, Peoples R China (författare)
Dou, Jin-HeShandong First Med Univ & Shandong Acad Med Sci, Peoples R China (författare)
Chen, YangYantai Univ, Peoples R China (författare)
Yantai Univ, Peoples R ChinaKonstruktionsmaterial (creator_code:org_t)

Av författaren/redakt...: Hu, Ji-Chong; Huang, Hai-Liang; Wu, Chong-Chong; Sun, Xiao-Yu; Wang, Jie; Yang, Yan-Hong; visa fler...; Qu, Jing-Long; Jiang, Liang; Dou, Jin-He; Chen, Yang; visa färre...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.