Jönsson, StinaLinköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan
(författare)
The effects of solvents on the morphology and sheet resistance in poly(3,4-ethylenedioxythiophene)–polystyrenesulfonic acid (PEDOT–PSS) films
- Artikel/kapitelEngelska2003
Förlag, utgivningsår, omfång ...
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:liu-46525
-
https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-46525URI
-
https://doi.org/10.1016/S0379-6779(02)01259-6DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Films of poly(3,4-ethylenedioxythiophene)–polystyrenesulfonic acid (PEDOT–PSS), prepared by coating the aqueous PEDOT–PSS dispersion and by coating a mixture of the PEDOT–PSS dispersion and different solvents, have been studied using four-point probe conductivity measurements, atomic force microscopy and photoelectron spectroscopy. The electrical conductivity of thin films of the second type (further on called PEDOT–PSS–solvents) was increased by a factor of about 600 as compared to films of the first type (further on called PEDOT–PSS–pristine). Morphological and physical changes occur in the polymer film due to the presence of the solvent mixture, the most striking being that the ratio of PEDOT-to-PSS in the surface region of the films is increased by a factor of ∼2–3. This increase of PEDOT at the surface indicates that the thickness of the insulating PSS ‘shell’ that surrounds the conducting PEDOT–PSS grains is reduced. The (partial) reduction of the excess PSS layer that surrounds the conducting PEDOT–PSS grains is proposed to lead to an increased and improved connectivity between such grains in the film and hence a higher conductivity. When PEDOT–PSS–solvents receives a post-coating heat treatment, the increased PEDOT-to-PSS ratio at the surface is maintained or even slightly improved, as is the increase in electrical conductivity, even though spectroscopy show that the solvent molecules are removed. This suggests that screening or doping by the solvents throughout the film are not likely to be the key mechanisms for the improved conductivity and supports our proposed mechanism of improved conductivity through improved connectivity between the conducting grains.
Ämnesord och genrebeteckningar
-
AFM
-
Conducting polymers
-
PEDOT-PSS
-
Polymer blend
-
Sorbitol
-
XPS
-
TECHNOLOGY
-
TEKNIKVETENSKAP
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Birgerson, J.Linköpings universitet,Institutionen för fysik, kemi och biologi,Tekniska högskolan
(författare)
-
Crispin, XavierLinköpings universitet,Institutionen för fysik, kemi och biologi,Tekniska högskolan(Swepub:liu)xavcr43
(författare)
-
Greczynski, GrzegorzLinköpings universitet,Institutionen för fysik, kemi och biologi,Tekniska högskolan(Swepub:liu)grzgr49
(författare)
-
Osikowicz, WojciechLinköpings universitet,Institutionen för fysik, kemi och biologi,Tekniska högskolan(Swepub:liu)wojos52
(författare)
-
Denier van der Gon, A.W.Denier van der Gon, A.W., Faculty of Applied Physics, Eindhoven University of Technology, Eindhoven, Netherlands
(författare)
-
Salaneck, William RLinköpings universitet,Institutionen för fysik, kemi och biologi,Tekniska högskolan(Swepub:liu)wilsa67
(författare)
-
Fahlman, MatsLinköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan(Swepub:liu)matfa21
(författare)
-
Linköpings universitetInstitutionen för teknik och naturvetenskap
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Synthetic metals139:1, s. 1-100379-67791879-3290
Internetlänk
Hitta via bibliotek
Till lärosätets databas