Measurement and modeling of residual stress in a welded Haynes® 25 cylinder

Larsson, CeciliaLinköpings universitet,Konstruktionsmaterial,Tekniska högskolan,Div. of Eng. Mat., Department of Mech. Eng., Linköping University, 58183 Linköping, Sweden (författare)

Validerad; 2005; 20100126 (ysko)
An experimental and simulation study of residual stresses was made in the vicinity of a gas tungsten arc weld, used to join a hemispherical end cap to a cylinder. The capped cylinder is used in a satellite application and was fabricated from a Co-based Haynes® 25 alloy. The cylinder was 34.7 mm in outer diameter and 3.3 mm in thickness. The experimental measurements were made by neutron diffraction and the simulation used the implicit Marc finite element code. The experimental resolution was limited to approximately 3 mm parallel to the axis of the cylinder (the weld was 6 mm in the same direction) and comparison over the same volume of the finite element prediction showed general agreement. Subject to the limited spatial resolution, the largest experimentally measured tensile residual stress was 180 MPa, located at the middle of the weld. However, the predictions suggest that there are regions in the weld where average tensile residual stresses as much as 400 MPa exist. One qualitative disparity between the model and the experiments was that the measurement included a larger degree of asymmetry on either side of the weld than predicted by the model.

Holden, T.M.Los Alamos National Laboratory, Los Alamos, NM 87545, USA (författare)
Bourke, M.A.M.Los Alamos National Laboratory, Los Alamos, NM 87545, USA (författare)
Stout, M.Los Alamos National Laboratory, Los Alamos, NM 87545, USA (författare)
Teague, J.Los Alamos National Laboratory, Los Alamos, NM 87545, USA (författare)
Lindgren, Lars-ErikHögskolan Dalarna,Luleå tekniska universitet,Material- och solidmekanik,Materialteknik(Swepub:du)lel (författare)
Linköpings universitetKonstruktionsmaterial (creator_code:org_t)

Ingår i:Materials Science & Engineering: Elsevier BV399:1-2, s. 49-570921-50931873-4936

Av författaren/redakt...: Larsson, Cecilia; Holden, T.M.; Bourke, M.A.M.; Stout, M.; Teague, J.; Lindgren, Lars-E ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

Av lärosätet: Linköpings universitet; Luleå tekniska universitet; Högskolan Dalarna

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.