Mesoporous silica templated zirconia nanoparticles

Ballem, Mohamed A.Linköpings universitet,Nanostrukturerade material,Tekniska högskolan (författare)

Nanoparticles of zirconium oxide (ZrO2)were synthesized by infiltration of a zirconia precursor(ZrOCl28H2O) into a SBA-15 mesoporous silicamold using a wet-impregnation technique. X-raydiffractometry and high-resolution transmission electronmicroscopy show formation of stable ZrO2nanoparticles inside the silica pores after a thermaltreatment at 550 C. Subsequent leaching out of thesilica template by NaOH resulted in well-dispersedZrO2 nanoparticles with an average diameter of*4 nm. The formed single crystal nanoparticles arefaceted with 110 surfaces termination suggesting it tobe the preferred growth orientation. A growth modelof these nanoparticles is also suggested.

Zirconia - Nanoparticles - Mesoporous silica - Wet-impregnation - Metal oxide - Synthesis - Nanomanufacturing
NATURAL SCIENCES
NATURVETENSKAP

Córdoba, JoséLinköpings universitet,Nanostrukturerade material,Tekniska högskolan (författare)
Odén, MagnusLinköpings universitet,Nanostrukturerade material,Tekniska högskolan(Swepub:liu)magod41 (författare)
Linköpings universitetNanostrukturerade material (creator_code:org_t)

Ingår i:Journal of nanoparticle research: SpringerLink13:7, s. 2743-27481388-07641572-896X

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.