Low Temperature Nanocasting of Ultrafine Hematite Nanoparticles using Mesoporous Silica Molds

Ballem, Mohamed A.Linköpings universitet,Nanostrukturerade material,Tekniska högskolan (författare)

Iron oxide (α-Fe2O3) nanoparticles with very small size, high crystallinity, and narrow size distribution were synthesized by infiltration of Fe(NO3)3.9H2O as an oxide precursor into mesoporous silica (SBA-15 and SBA-16) molds using a wetimpregnation technique. High resolution transmission electron microscopy shows that during the hydrothermal treatment of the precursor at 140 °C for 2 days, stable α-Fe2O3 nanoparticles inside the silica pores are formed. Subsequent leaching out of the silica template by NaOH resulted in well dispersed nanoparticles with an average diameter of ~ 4 nm.

Zhang, XuanjunLinköpings universitet,Tekniska högskolan,Tillämpad Fysik(Swepub:liu)xuazh91 (författare)
Johansson, Emma M.Linköpings universitet,Nanostrukturerade material,Tekniska högskolan(Swepub:liu)emmjo89 (författare)
Córdoba, José M.Linköpings universitet,Nanostrukturerade material,Tekniska högskolan(Swepub:liu)josco23 (författare)
Odén, MagnusLinköpings universitet,Nanostrukturerade material,Tekniska högskolan(Swepub:liu)magod41 (författare)
Linköpings universitetNanostrukturerade material (creator_code:org_t)

Av författaren/redakt...: Ballem, Mohamed ...; Zhang, Xuanjun; Johansson, Emma ...; Córdoba, José M.; Odén, Magnus