Composition tunable Al1-xInxN nanorod arrays grown by ultra-high-vacuum magnetron sputter epitaxy

• Self-assembled ternary Al1-xInxN nanorod arrays with variable In concentration, 0.10 ≤ x ≤ 0.32 have been realized onto c-plane sapphire substrates by ultra-high-vacuum magnetron sputter epitaxy with Ti0.21Zr0.79N or VN seed layers assistance. The formation of nanorods was very sensitive to the applied seed layer. Without proper seed layer assistance a continuous Al1-xInxN film was grown. The nanorods exhibit hexagonal crosssections with preferential growth along the c axis. A coaxial rod structure with higher In concentration in the core was observed by (scanning) transmission electron microscopy in combination with low-loss electron energy loss spectroscopy and energy dispersive xray spectroscopy. 5 K cathodoluminescence spectroscopy of Al0.86In0.14N nanorods revealed band edge emission at ~5.46 eV, which was accompanied by a strong defectrelated emission at ~ 3.38 eV.

Nyckelord

NATURAL SCIENCES

NATURVETENSKAP

Publikations- och innehållstyp

vet (ämneskategori)

ovr (ämneskategori)