CVD growth of 3C-SiC on 4H-SiC substrate

Henry, AnneLinköpings universitet,Halvledarmaterial,Tekniska högskolan (författare)

The hetero epitaxial growth of 3C-SiC on nominally on-axis 4H-SiC is reported. A horizontal hot-wall CVD reactor working at low pressure is used to perform the growth experiments in a temperature range of 1200-1500 °C with the standard chemistry using silane and propane as precursors carried by a mix of hydrogen and argon. The optimal temperature for single-domain growth is found to be about 1350 °C. The ramp up-conditions and the gas-ambient atmosphere when the temperature increases are key factors for the quality of the obtained 3C layers. The best pre-growth ambient found is carbon rich environment; however time of this pre-treatment is crucial. A too high C/Si ratio during growth led to polycrystalline material whereas for too low C/Si ratios Si cluster formation is observed on the surface. The addition of nitrogen gas is also explored.

Li, XunLinköpings universitet,Halvledarmaterial,Tekniska högskolan(Swepub:liu)xunli87 (författare)
Leone, StefanoLinköpings universitet,Halvledarmaterial,Tekniska högskolan(Swepub:liu)stele19 (författare)
Kordina, OlofLinköpings universitet,Halvledarmaterial,Tekniska högskolan(Swepub:liu)ollko50 (författare)
Janzén, ErikLinköpings universitet,Halvledarmaterial,Tekniska högskolan(Swepub:liu)erija14 (författare)
Linköpings universitetHalvledarmaterial (creator_code:org_t)

Av författaren/redakt...: Henry, Anne; Li, Xun; Leone, Stefano; Kordina, Olof; Janzén, Erik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.