Fager, HannaLinköpings universitet,Tunnfilmsfysik,Tekniska högskolan
(författare)
Growth and Properties of Amorphous Hf1−x−yAlxSiyN (0≤x≤0.2; 0≤y≤0.2) and a-Hf0.6Al0.2Si0.2N/nc-HfN Multilayers by DC Reactive Magnetron Sputtering from a Single Hf0.60Al0.20Si0.20 Target
Förlag, utgivningsår, omfång ...
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:liu-80207
-
https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-80207URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:vet swepub-contenttype
-
Ämneskategori:ovr swepub-publicationtype
Anmärkningar
-
Amorphous (a) and nanocrystalline (nc) Hf1−x−yAlxSiyN and multilayer a-Hf0.6Al0.2Si0.2N/nc-HfN films are grown on Si(001) at temperatures Ts = 100-450 ◦C using ultrahigh vacuum magnetically-unbalanced reactive magnetron sputtering from a single Hf0.60Al0.20Si0.20 target in a 5%-N2/Ar atmosphere at a total pressure of 20 mTorr (2.67 Pa). The composition and nanostructure of Hf1−x−yAlxSiyN is controlled during growth by independently varying the ion energy (Ei) and the ion-to-metal flux ratio (Ji/JMe) incident at the film surface. With Ji/JMe = 8, the composition and nanostructure of the films ranges from x-ray amorphous with 1-x-y = 0.60 at Ei = 15 eV, to an amorphous matrix with encapsulated nanocrystals with 1-x-y = 0.66-0.84 at Ei = 25-35 eV, to nanocrystalline with 1-x-y = 0.96-1.00 at Ei = 45-65 eV. Varying Ji/JMe with Ei = 13 eV yields amorphous alloy films at Ts = 100 ◦C. a-Hf0.6Al0.6Si0.6N/nc-HfN multilayers with periods Λ = 2-20 nm exhibit enhanced fracture toughness compared to polycrystalline VN, TiN, and Ti0.5Al0.5N reference samples; multilayer hardness values increase monotonically from 20 GPa with Λ = 20 nm to 27 GPa with Λ = 2 nm.
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Andersson, J. M.Seco Tools AB, SE-737 82 Fagersta, Sweden
(författare)
-
Mei, A.R.B.Frederick Seitz Materials Research Laboratory and Materials Science Department, University of Illinois, USA
(författare)
-
Howe, B.M.Air Force Research Laboratory, Materials and Manufacturing Directorate, Wright-Patterson AFB, Ohio, USA
(författare)
-
Greene, Joseph ELinköpings universitet,Tunnfilmsfysik,Tekniska högskolan(Swepub:liu)josgr17
(författare)
-
Petrov, IvanLinköpings universitet,Tunnfilmsfysik,Tekniska högskolan(Swepub:liu)ivape26
(författare)
-
Hultman, LarsLinköpings universitet,Tunnfilmsfysik,Tekniska högskolan(Swepub:liu)larhu75
(författare)
-
Linköpings universitetTunnfilmsfysik
(creator_code:org_t)
Internetlänk