Pore Condensation in Glycerol Dehydration : Modification of a Mixed Oxide Catalyst

• Pore condensation has been suggested as an initiator of deactivation in the dehydration of glycerol to acrolein. To avoid potential pore condensation of the glycerol, a series of WO3supported on ZrO2 catalysts have been prepared through thermal sintering, with modified pore systems. It was shown that catalysts heat treated at temperatures above 800 °C yielded suitable pore system and the catalyst also showed a substantial increase in acrolein yield. The longevity of the heat-treated catalysts was also improved, indeed a catalyst heat treated at 850 °C displayed significantly higher yields and lower pressure-drop build up over the 600 h of testing. Further, the catalyst characterisation work gave evidence for a transition from monoclinic to triclinic tungsten oxide between 850 and 900 °C. There is also an increase in acid-site concentration of the heat-treated catalysts. Given the improved catalyst performance after heat-treatment, it is not unlikely that pore condensation is a significant contributing factor in catalyst deactivation for WO3 supported on ZrO2 catalysts in the glycerol dehydration reaction.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Kemiska processer (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Chemical Process Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering (hsv//eng)

Nyckelord

Glycerol

Pore Condensation

Dehydration

Acrolein

Deactivation

Bioenergiteknik/Energi- och Miljöteknik

Bioenergy Technology

Acrolein

Deactivation

Dehydration

Glycerol

Pore condensation

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)