Naphthenic acid corrosion characteristic and corrosion product film resistance of carbon steel and Cr5Mo low alloy steel in secondary vacuum gas oil
-
- Liu, G.Q. (författare)
- School of Materials Science & Engineering, Beifang University of Nationalities, Yinchuan, Ningxia
-
- Zhang, X.L. (författare)
- School of Materials Science & Engineering, Beifang University of Nationalities, Yinchuan, Ningxia
-
- Qu, D.R. (författare)
- SINOPEC Research Institute of Safety Engineering
-
visa fler...
-
- Zheng, Y.G. (författare)
- State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences
-
- Jiang, S.L. (författare)
- State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences
-
- Jiang, X. (författare)
- SINOPEC Research Institute of Safety Engineering
-
- Yang, Qixing (författare)
- Luleå tekniska universitet,Mineralteknik och metallurgi
-
- Han, F.L. (författare)
- School of Materials Science & Engineering, Beifang University of Nationalities, Yinchuan, Ningxia
-
visa färre...
-
(creator_code:org_t)
- 2016
- 2016
- Engelska.
-
Ingår i: Corrosion Engineering, Science and Technology. - 1478-422X .- 1743-2782. ; 51:6, s. 445-454
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Although naphthenic acid corrosion (NAC) has been studied for many years, the mechanism of NAC is not fully understood. The objective of this paper is to study high-temperature NAC in secondary vacuum gas oil of an industrial crude oil vacuum distillation tower. A high-temperature autoclave was applied to conduct high-temperature corrosion test to investigate NAC behaviour of carbon steel and Cr5Mo low alloy steel at different sulphur contents and total acid numbers (TAN). The result shows that the corrosion rate of carbon steel and low alloy steel is high at low TAN and high TAN while it keeps at a low value at medium TAN. Corrosion product film on Cr5Mo low alloy steel surface is denser and more compact than that of carbon steel at high TAN. The chromium present in Cr5Mo low alloy steel plays an important role in NAC resistance by the formation of Cr7S8 film in the inner layer of the scale. Corrosion rates of the two steels in secondary vacuum gas oil are high at low TAN and high TAN, but low at medium TAN which are strange and different from previous experimental results conducted in non-industrial oil solution. A tentative explanation for this new phenomenon is also put forward.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Process Metallurgy
- Processmetallurgi
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas