Solidification behaviour and phase constituents of cast Mg-Zn-misch metal alloys
-
- Wei, Liu-Ying (författare)
- Luleå tekniska universitet
-
- Dunlop, G.L. (författare)
- CRC for Alloy and Solidification Technology (CAST), Department of Mining and Metallurgical Engineering, The University of Queensland
-
- Westengen, H. (författare)
- Norsk Hydro a.s., Research Centre Porsgrunn
-
(creator_code:org_t)
- 1997
- 1997
- Engelska.
-
Ingår i: Journal of Materials Science. - 0022-2461 .- 1573-4803. ; 32:12, s. 3335-3340
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The solidification path and phase constituents of alloys in the magnesium-rich corner of the Mg-Zn-misch metal (MM) pseudo-ternary system have been investigated by a combination of differential thermal analysis, analytical electron microscopy and X-ray diffraction. The solidification behaviour diagram for this system was found to be dominated by a large two-phase ( -Mg plus T-phase) field in which the lowest eutectic temperature was 500°C. T-phase has a c-centred orthorhombic crystal structure and exhibits a wide range of stoichiometry. The interdendritic eutectic phase in the pseudo-binary Mg-MM system is Mg12MM which has the same b c t structure as Mg12Ce. The eutectic temperature here is 593°C.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Nyckelord
- Material Mechanics
- Materialmekanik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas