Adhesion enhancement of diamond coatings on WC tools by high energy ion irradiation

• Microcrystalline diamond thin films were deposited on cemented tungsten carbide cutting tools by hot-filament chemical vapour deposition process. The coatings deposited were irradiated with 50 MeV Si7+ ions upto a dose of <1013 ions cm-2. The adhesion and wear characteristics of as-deposited and irradiated coatings were studied and it was found that irradiation induced increased adhesion of the coatings to the substrate resulting in reduced coating failure during wear tests.