Preparation of Na0.5K0.5NbO3/La0.6Sr0.2Mn1.2O3/LaAlO3 Thin Film Structures by Pulsed Laser Deposition
-
- Cho, Choong-Rae (författare)
- Department of Condensed Matter Physics, Royal Institute of Technology, SE-100 44 Stockholm, Sweden
-
- Khartsev, S.I. (författare)
- Department of Condensed Matter Physics, Royal Institute of Technology, SE-100 44 Stockholm, Sweden
-
- Grishin, A.M. (författare)
- Department of Condensed Matter Physics, Royal Institute of Technology, SE-100 44 Stockholm, Sweden
-
visa fler...
-
- Lindbäck, Ture (författare)
- Luleå tekniska universitet
-
visa färre...
-
(creator_code:org_t)
- Warrendale, Pa : Materials Research Society, 1999
- 1999
- Engelska.
-
Ingår i: Multicomponent oxide films for electronics. - Warrendale, Pa : Materials Research Society. - 1558994815 - 9781558994812 ; , s. 249-254
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- We report on ferroelectric/giant magnetoresistive Nao.sKo.sNbCVLao.oSrojMniO} (NKN/LSMO) heterostructures gro\vn onto LaAlOj (001) single crystal using KrF pulsed laser ablation of stoichiometric ceramic target. Main processing parameters have been optimized to obtain smooth LSMO template layer, avoid NKN-LSMO interdiffusion, preserve NKN stoichiometry against the lost of volatile potassium and sodium and achieve reasonable reliability of NKN film performance. X-ray diffraction 0- 20 scans and rocking curves evidence for single-phase content and high c-axis orientation both in template LSMO and top NKN layers. Ferroelectric measurements yield remnant polarization P, of 1.5 (.iC/cm2 and spontaneous polarization Ps of 7 jiC/cm2 at electric field strength of 130 kV/cm. At room temperature, dielectric permittivity e' and dissipation factor tancJhave been found to vary from 595 to 555 and 0.046 to 0.029 respectively in the frequency range of 0.4 to 20 kHz. At 10 kHz dielectric permittivity linearly increases from 410 to 650 in the temperature range 77 K to 415 K while the dissipation factor below 320 K does not exceed 3%.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Kompositmaterial och -teknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Composite Science and Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Nyckelord
- Polymeric Composite Materials
- Polymera konstruktionsmaterial
- Engineering Materials
- Materialteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- kon (ämneskategori)
Hitta via bibliotek
Till lärosätets databas