Transverse single-fibre test for interfacial debonding in composites : 1. Experimental observations
- Artikel/kapitelEngelska1997
Förlag, utgivningsår, omfång ...
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:ltu-3451
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-3451URI
-
https://doi.org/10.1016/S1359-835X(96)00123-6DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Godkänd; 1997; 20070509 (cira)
-
Micromechanical methods for studies of interfacial debonding in fibre composites provide the possibility of comparing different materials. Since most previous composite studies focus on shear loading of the fibre matrix interface, the debonding process in single-fibre glass fibre/epoxy composites was studied in situ by optical microscopy during transverse tensile loading. Specimens had cylindrical debond cracks of known dimensions created in fragmentation tests. Mechanisms for debond growth were described for two materials where the difference was in glass fibre surface treatment. As the debonds reached a critical size in the arc (circumferential) direction, unstable debond growth occurred in the fibre direction. The debond angle at instability was fairly similar for both materials, although the material based on glass fibre treated with a coupling agent reached twice as high stress before instability.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Ericson, M.L.Luleå tekniska universitet
(författare)
-
Varna, JanisLuleå tekniska universitet,Materialvetenskap(Swepub:ltu)janis
(författare)
-
Berglund, Lars A.Luleå tekniska universitet
(författare)
-
Luleå tekniska universitetMaterialvetenskap
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Composites. Part A, Applied science and manufacturing28:4, s. 309-3151359-835X1878-5840
Internetlänk
Hitta via bibliotek
Till lärosätets databas