AEM investigation of ceramic/incology 909 diffusional reactions after joining by HIP

Godkänd; 1994; 20070426 (cira)
Diffusion bonding by hot isostatic pressing (HIP) was performed between Incoloy 909 and five different ceramics. Two of the ceramics were composites made from powder mixtures of Si3N4 and either 60 vol% TiN or 50 vol% TiB2, while three were monolithic materials, namely Si3N4 with 2.5 wt% Y2O3 as a sintering additive, Si3N4 without additives, and Si2 N2O without additives. A diffusion couple geometry was developed to facilitate the preparation of thin-foil specimens for examination by analytical electron microscopy (AEM). Diffusion bonding was performed by HIP at 927°C (1200K) and 200 MPa for 4 h. The formation of reaction layers was very limited, being less than 1 μm in total layer thickness. Two reaction products were found by AEM; a continuous, very thin, (≤100 nm) layer of fine TiN crystals at the initial ceramic/metal interface, and larger grains extending about 100–500 nm into the superalloy and forming a semi-continuous layer of a G-phase suicide containing mainly nickel, silicon and niobium.

Wei, L.-YLuleå tekniska universitet (författare)
Loberg, Bengt (författare)
Olsson, M.Department of Materials Science, Uppsala University (författare)
Johansson, S.Department of Materials Science, Uppsala University (författare)
Luleå tekniska universitetDepartment of Materials Science, Uppsala University (creator_code:org_t)

Av författaren/redakt...: Larker, Rickard; Wei, L.-Y; Loberg, Bengt; Olsson, M.; Johansson, S.

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.