Improvement of critical current density in the Bi-Pb-Sr-Ca-Cu-O system through hot isostatic pressing

• The effects of hot isostatic pressing (HIPing) on densification and the superconducting properties of the Bi-Pb-Sr-Ca-O system were investigated. A relative density up to 95% and a critical current density greater than 1100 A/cm2 at 77 K were achieved through HIPing at 650°C for 2 h under 200 MPa argon. Under these conditions, the product gave a value of Jc four times that without HIPing. To was unaffected by HIPing for samples encapsulated with a combination of glass and silver tubes. However, To was suppressed from 103 K to 86 K for samples encapsulated with stainless steel and silver tubes while Jc increased from 260 A/ cm2 to 1086 A/cm2 during HIPing, indicating that the weak links were significantly improved. A new minor phase, having a composition of Bi/Pb/Sr/Ca/Cu=0.58/2.8/3.0/2.1/1.1, was observed in HIPed samples but its effect on Jc is not clear

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

Engineering Materials

Materialteknik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)