C@TiO2 core-shell adsorbents for efficient rhodamine B adsorption from aqueous solution
- Article/chapterEnglish2021
Publisher, publication year, extent ...
-
Elsevier,2021
-
printrdacarrier
Numbers
-
LIBRIS-ID:oai:DiVA.org:ltu-83930
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-83930URI
-
https://doi.org/10.1016/j.micromeso.2021.111110DOI
Supplementary language notes
-
Language:English
-
Summary in:English
Part of subdatabase
Classification
-
Subject category:ref swepub-contenttype
-
Subject category:art swepub-publicationtype
Notes
-
Validerad;2021;Nivå 2;2021-05-03 (alebob);Finansiär: Priority Academic Program Development of Jiangsu Higher Education Institutions
-
In the present work, C@TiO2 core-shell adsorbents were successfully prepared and the adsorption capacities for rhodamine B (RB) were investigated at different conditions. The adsorbents were prepared by first in-situ hydrolysis and deposition of TBOT on the surface of ZIF-8 nanoparticles to obtain ZIF-8@titania gel, and then carbonization. XRD, SEM, TEM, and N2 adsorption-desorption techniques were employed to characterize the adsorbents. The results showed that the adsorbents were comprised of TiO2 shell and carbon core. Large surface area and hierarchical pores, which were different from ZIF-8 derived porous carbon, were generated due to the less contraction of carbon during carbonization when robust TiO2 shell covered on the surface. The highest adsorption capacity for RB was 298 mg/g on C@TiO2. Apart from the hierarchical pores and large surface area, the low surface charge of C@TiO2 core-shell adsorbents was also observed, which also contributed to the high adsorption capacity for cationic dyes. The reuse experiments showed that the adsorbents maintained the high adsorption capacity after 5 cycles. The high stability is crucial for practical application.
Subject headings and genre
Added entries (persons, corporate bodies, meetings, titles ...)
-
Yu, Liang,1986-Luleå tekniska universitet,Kemiteknik(Swepub:ltu)liayut
(author)
-
Cai, JuanjuanState Key Laboratory of Materials-Oriented Chemical Engineering, College of Chemistry and Chemical Engineering, Nanjing Tech University, Nanjing, 211816, China
(author)
-
Zhang, LixiongState Key Laboratory of Materials-Oriented Chemical Engineering, College of Chemistry and Chemical Engineering, Nanjing Tech University, Nanjing, 211816, China
(author)
-
State Key Laboratory of Materials-Oriented Chemical Engineering, College of Chemistry and Chemical Engineering, Nanjing Tech University, Nanjing, 211816, ChinaKemiteknik
(creator_code:org_t)
Related titles
-
In:Microporous and Mesoporous Materials: Elsevier3201387-18111873-3093
Internet link
Find in a library
To the university's database