Synthesis of mesoporous silica by a surface charge reversal route

Validerad; 2010; 20100528 (ysko)
Pore size adjustable mesoporous silica was synthesized by adsorption of varying amount of sodium dodecyl benzenesulfonate at the surface of silica activated by zinc ion via a novel surface charge reversal route. The pore size and volume can be adjusted from 5.9 to 13.76 nm and 0.88 to 1.08 cm3·g-1 respectively with increasing the SDBS concentration from 0.77 to 3.08 mmol·L-1. Adsorption of Zn2+ as a function of pH and N2 adsorption/desorption isotherms demonstrated that the metal ions such as Zn2+ could be readily removed with dilute nitric acid without apparent collapse of the pore structure at the proper range of SDBS concentration.

Liu, JiaUniversity of Jinan (författare)
Sun, Zhong-XiUniversity of Jinan (författare)
Fan, Bao-QiangUniversity of Jinan (författare)
Yang, Zhen-DongUniversity of Jinan (författare)
Forsling, WillisLuleå tekniska universitet,Industriell miljö- och processteknik(Swepub:ltu)wifo (författare)
University of JinanIndustriell miljö- och processteknik (creator_code:org_t)

Ingår i:Journal of Colloid and Interface Science: Elsevier BV349:2, s. 473-4760021-97971095-7103

Av författaren/redakt...: Zhang, Wei-Min; Liu, Jia; Sun, Zhong-Xi; Fan, Bao-Qiang; Yang, Zhen-Dong; Forsling, Willis

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.