High-speed X-ray study of process dynamics caused by surface features during continuous-wave laser polishing

• During high-speed X-ray imaging of laser surface polishing experiments of specimens of 316L stainless steel at Argonne National Lab's Advanced Photon Source, it was discovered that the induced keyhole changes shape and dimensions while crossing an engineered surface feature without altering process parameters. It was observed that the post-surface feature keyhole was deeper than that of the pre surface feature keyhole. This work reports on the first in-situ observation of the effect of localized surface geometry on underlying melt pool behavior. This has implications for defect formation mechanisms during laser melting processes that rely on melt pool geometry.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

Nyckelord

Laser

Polishing

X-ray imaging

Produktionsutveckling

Manufacturing Systems Engineering

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)