InGaN Platelets : Synthesis and Applications toward Green and Red Light-Emitting Diodes

• In this work, we present a method to synthesize arrays of hexagonal InGaN submicrometer platelets with a top c-plane area having an extension of a few hundred nanometers by selective area metal-organic vapor-phase epitaxy. The InGaN platelets were made by in situ annealing of InGaN pyramids, whereby InGaN from the pyramid apex was thermally etched away, leaving a c-plane surface, while the inclined {101Ì1} planes of the pyramids were intact. The as-formed c-planes, which are rough with islands of a few tens of nanometers, can be flattened with InGaN regrowth, showing single bilayer steps and high-quality optical properties (full width at half-maximum of photoluminescence at room temperature: 107 meV for In 0.09 Ga 0.91 N and 151 meV for In 0.18 Ga 0.82 N). Such platelets offer surfaces having relaxed lattice constants, thus enabling shifting the quantum well emission from blue (as when grown on GaN) to green and red. For single InGaN quantum wells grown on the c-plane of such InGaN platelets, a sharp interface between the quantum well and the barriers was observed. The emission energy from the quantum well, grown under the same conditions, was shifted from 2.17 eV on In 0.09 Ga 0.91 N platelets to 1.95 eV on In 0.18 Ga 0.82 N platelets as a result of a thicker quantum well and a reduced indium pulling effect on In 0.18 Ga 0.82 N platelets. On the basis of this method, prototype light-emitting diodes were demonstrated with green emission on In 0.09 Ga 0.91 N platelets and red emission on In 0.18 Ga 0.82 N platelets.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Nanoteknik -- Nanoteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Nano-technology -- Nano-technology (hsv//eng)

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Keyword

InGaN

light-emitting diodes

metal-organic vapor-phase epitaxy

platelets

selective area growth

Diodes

Gallium nitride

III-V semiconductors

Lattice constants

Light emitting diodes

Metallorganic vapor phase epitaxy

Optical properties

Organometallics

Semiconductor alloys

Emission energies

Green emissions

In-situ annealing

InGaN quantum wells

Metal-organic vapor phase epitaxy

Quantum well emission

Semiconductor quantum wells

InGaN

light-emitting diodes

metal-organic vapor-phase epitaxy

platelets

selective area growth

Publication and Content Type

ref (subject category)

art (subject category)