Construction of Mesoporous Frameworks with Vanadoborate Clusters

Chen, HongStockholms universitet,Institutionen för material- och miljökemi (MMK),China University of Geosciences, Wuhan (författare)

AuthorCount:6;
A new porous vanadoborate was synthesized by employing the scale chemistry theory with the vanadoborate cluster V10B28. The twofold interpenetrated lvt network was assembled with zinc-containing elliptical vanadoborate clusters and Zn polyhedra. The single lvt framework contains a three-dimensional 38x38x20 ring channel system with the pore size (24.7x12.7 angstrom) reaching the mesoscale, thus indicating the possibility of constructing 3D ordered mesopores with vanadoborate clusters. The porosity of the SUT-7 structure was confirmed by CO2 adsorption of the as-synthesized materials.

Yu, Zheng-Bao (författare)
Bacsik, ZoltanStockholms universitet,Institutionen för material- och miljökemi (MMK)(Swepub:su)zbacs (författare)
Zhao, HuishuangStockholms universitet,Institutionen för material- och miljökemi (MMK) (författare)
Yao, QingxiaStockholms universitet,Institutionen för material- och miljökemi (MMK) (författare)
Sun, JunliangStockholms universitet,Institutionen för material- och miljökemi (MMK),Peking University, China(Swepub:su)jsun (författare)
Stockholms universitetInstitutionen för material- och miljökemi (MMK) (creator_code:org_t)

Ingår i:Angewandte Chemie International Edition: Wiley53:14, s. 3608-36111433-78511521-3773

Av författaren/redakt...: Chen, Hong; Yu, Zheng-Bao; Bacsik, Zoltan; Zhao, Huishuang; Yao, Qingxia; Sun, Junliang

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.