Preparation of graded silicalite-1 substrates for all-zeolite membranes with excellent CO2/H-2 separation performance

• Graded silicalite-1 substrates with a high gas permeability and low surface roughness have been produced by pulsed current processing of a thin coating of a submicron silicalite-1 powder onto a powder body of coarser silicalite-1 crystals. Thin zeolite films have been hydrothermally grown onto the graded silicalite-1 support and the all-zeolite membranes display an excellent CO2/H-2 separation factor of 12 at 0 degrees C and a CO2 permeance of 21.3 x 10(-7) mol m(-2) s(-1) Pa-1 for an equimolar CO2/H-2 feed at 505 kPa and 101 kPa helium sweep gas. Thermal cracking estimates based on calculated surface energies and measured thermal expansion coefficients suggest that all-zeolite membranes with a minimal thermal expansion mismatch between the graded substrate and the zeolite film should remain crack-free during thermal cycling and the critical calcination step.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering (hsv//eng)

NATURVETENSKAP  -- Kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Kemiska processer (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Chemical Process Engineering (hsv//eng)

Nyckelord

All-zeolite membranes

Membrane separation

Gas separation

Cracking

Thermal cycling

Engineering Materials

Chemical Technology

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)