Water as the Key to Proto-Aragonite Amorphous CaCO3

Temperature and pH value can affect the short-range order of proto-structured and additive-free amorphous calcium carbonates (ACCs). Whereas a distinct change occurs in proto-vaterite (pv) ACC above 45 degrees C at pH 9.80, proto-calcite (pc) ACC (pH 8.75) is unaffected within the investigated range of temperatures (7-65 degrees C). IR and NMR spectroscopic studies together with EXAFS analysis showed that the temperature-induced change is related to the formation of proto-aragonite (pa) ACC. The data strongly suggest that the binding of water molecules induces dipole moments across the carbonate ions in pa-ACC as in aragonite, where the dipole moments are due to the symmetry of the crystal structure. Altogether, a (pseudo-)phase diagram of the CaCO3 polyamorphism in which water plays a key role can be formulated based on variables of state, such as the temperature, and solution parameters, such as the pH value.

Chevrier, Daniel M. (författare)
Zhang, Peng (författare)
Hedin, NiklasStockholms universitet,Institutionen för material- och miljökemi (MMK)(Swepub:su)nhedi (författare)
Gebauer, Denis (författare)
Stockholms universitetInstitutionen för material- och miljökemi (MMK) (creator_code:org_t)

Ingår i:Angewandte Chemie International Edition: Wiley55:28, s. 8117-81201433-78511521-3773

Av författaren/redakt...: Farhadi-Khouzani ...; Chevrier, Daniel ...; Zhang, Peng; Hedin, Niklas; Gebauer, Denis

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.