Electrochemical Denitrification and Oxidative Dehydrogenation of Ethylbenzene over N-doped Mesoporous Carbon : Atomic Level Understanding of Catalytic Activity by N-15 NMR Spectroscopy

Szewczyk, Ireneusz (författare)
Rokicińska, Anna (författare)
Michalik, Marek (författare)
visa fler...
Chen, Jianhong (författare)
Stockholms universitet,Institutionen för material- och miljökemi (MMK)
Jaworski, Aleksander (författare)
Stockholms universitet,Institutionen för material- och miljökemi (MMK)
Aleksis, Rihards (författare)
Stockholms universitet,Institutionen för material- och miljökemi (MMK)
Pell, Andrew J. (författare)
Stockholms universitet,Institutionen för material- och miljökemi (MMK)
Hedin, Niklas (författare)
Stockholms universitet,Institutionen för material- och miljökemi (MMK)
Slabon, Adam (författare)
Stockholms universitet,Institutionen för material- och miljökemi (MMK)
Kuśtrowski, Piotr (författare)
visa färre...
 (creator_code:org_t)
2020-08-03
2020
Engelska.
Ingår i: Chemistry of Materials. - : American Chemical Society (ACS). - 0897-4756 .- 1520-5002. ; 32:17, s. 7263-7273
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • Spherical mesoporous carbon (with a particle size in the range of 40−75 μm) was synthesized by nanoreplication of a hard silica template using sucrose as the carbon precursor. The mesoporous carbon with BET surface areas higher than 1200 m2/g was doped with N by a treatment in an aqueous solution of nitric acid and/or in a flow of gaseous ammonia. The highest N content (3.2 wt % of N in bulk) was obtained when both modification methods were combined. Complementary physicochemical characterization techniques, including scanning electron microscopy (SEM), low-temperature N2 adsorption, powder X-ray diffraction (XRD), and Raman spectroscopy revealed the morphology, structure, and textural properties of the synthesized N-loaded carbon materials. For the identification of the detailed chemical structure on the surface of the carbons, 1H, 13C, and 15N solid-state nuclear magnetic resonance (NMR) measurements were performed, and the data were supported by chemical shift calculations with accurate quantum chemistry methods and X-ray photoelectron spectroscopic (XPS) analyses. All NMR experiments were performed at natural isotope abundance. The verified experimental data clearly showed that after the introduction of the N-containing moieties by the combined methods of treatment, a high concentration of pyridinic N at the edge, and pyrrolic N being external to the edge, was achieved for the mesoporous carbon. The distributed N surface species promoted the catalytic activity in the oxidative dehydrogenation of ethylbenzene to styrene but did not significantly influence the efficiency of the carbon materials in the electrochemical reduction of nitrate ions.

Ämnesord

NATURVETENSKAP  -- Kemi (hsv//swe)
NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)

Publikations- och innehållstyp

ref (ämneskategori)
art (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy