High-Pressure Structures of α- and δ-ZrMo2O8

Krogh Andersen, A.M.Stockholms universitet,Institutionen för fysikalisk kemi, oorganisk kemi och strukturkemi,University of Southern Denmark (författare)

In situ high-pressure synchrotron X-ray powder diffraction studies of trigonal α-ZrMo2O8, zirconium molybdate, have been performed from ambient conditions to 1.9 GPa, over the α–δ phase transition at 1.06–1.11 GPa. The monoclinic structure of δ-ZrMo2O8, stable between 1.1 and 2.5 GPa at 298 K, has been solved by direct methods and refined using the Rietveld method. Significant distortions of the ZrO6 and MoO4 polyhedral elements are observed for δ-ZrMo2O8, as compared to the ambient conditions of the α-phase, while the packing of anions becomes more symmetric at high pressure.

Carlson, StefanLund University,Lunds universitet,MAX IV-laboratoriet,MAX IV Laboratory,European Synchrotron Radiation Facility(Swepub:lu)inor-sca (författare)
Stockholms universitetInstitutionen för fysikalisk kemi, oorganisk kemi och strukturkemi (creator_code:org_t)

Ingår i:Acta Crystallographica Section B Structural science: Wiley57:1, s. 20-260108-7681

Om ämnet

MEDICIN OCH HÄLSOVETENSKAP: MEDICIN OCH HÄLS ...; och Medicinska och f ...; och Andra medicinska ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.