Low temperature consolidated lead-free ferroelectric niobateceramics with improved electrical properties

• There is a concerted effort to develop lead-free piezoelectric ceramics. ((Na0.5K0.5)NbO3 based ceramics have good electrical properties, and are a potential replacement material for lead zirconate titanate piezoelectric ceramics. In this work a commercial powder based on (Na0.5K0.5)NbO3 with an initial particle size of 260 nm was consolidated by plasma sintering (SPS). To avoid volatilization, high mechanical pressures were used to minimize the densification temperature. It was found that under a uniaxial pressure of 100 MPa, fully densified compacts can be prepared at 850. Ceramics densified at such a low temperature demonstrate an unusually high remanent polarization (30 mC/cm2) and high d33 (146 pC/N). The improved ferroelectric properties are ascribed to the homogeneous, dense, and submicron grained microstructure achieved.

Ämnesord

NATURVETENSKAP  -- Kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)

Nyckelord

Chemistry

Kemi

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)