Microstructure homogeneity control in spark plasma sintering of Al2O3 ceramics

Wang, CaoStockholms universitet,Institutionen för material- och miljökemi (MMK),Department of Materials and Environmental Chemistry, Stockholm University (författare)

QC 20120214
Homogeneous microstructure control in the SPS (spark plasma sintering) sintered big size Al2O3 ceramic was realized by the synergy effect of grain boundary tailoring and proper pressure profile design. Two-step pressure profile itself did not show any efficient densification enhancement if no grain boundary modifier MgO added. The two-step pressure profile can effectively reduce average grain size and grain size difference over the sintered specimen, while MgO doping can reduce the average grain size in the whole sintered samples. Finally, a general strategy to overcome the intrinsic temperature gradient in SPS is suggested.

Wang, XinStockholms universitet,Institutionen för material- och miljökemi (MMK),School of Science, Hangzhou Dianzi University, China (författare)
Zhao, ZheStockholms universitet,Institutionen för material- och miljökemi (MMK),Department of Materials and Environmental Chemistry(Swepub:kth)u1qw3zev (författare)
Stockholms universitetInstitutionen för material- och miljökemi (MMK) (creator_code:org_t)

Ingår i:Journal of the European Ceramic Society: Elsevier BV31:1-2, s. 231-2350955-22191873-619X

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Keramteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.