Hydrogen storage in high surface area graphene scaffolds

Using an optimized KOH activation procedure we prepared highly porous graphene scaffold materials with SSA values up to 3400 m2 g−1 and a pore volume up to 2.2 cm3 g−1, which are among the highest for carbon materials. Hydrogen uptake of activated graphene samples was evaluated in a broad temperature interval (77–296 K). After additional activation by hydrogen annealing the maximal excess H2 uptake of 7.5 wt% was obtained at 77 K. A hydrogen storage value as high as 4 wt% was observed already at 193 K (120 bar H2), a temperature of solid CO2, which can be easily maintained using common industrial refrigeration methods.

Mercier, GuillaumeUmeå universitet,Institutionen för fysik(Swepub:umu)gume0003 (författare)
Sharifi, TivaUmeå universitet,Institutionen för fysik(Swepub:umu)tish0004 (författare)
Baburin, Igor A.Technische Universität Dresden, Theoretische Chemie, Bergstraße 66b, 01062 Dresden, Germany (författare)
Seifert, GotthardTechnische Universität Dresden, Theoretische Chemie, Bergstraße 66b, 01062 Dresden, Germany (författare)
Talyzin, Alexandr V.,1969-Umeå universitet,Institutionen för fysik(Swepub:umu)alta0001 (författare)
Umeå universitetInstitutionen för fysik (creator_code:org_t)

Ingår i:Chemical Communications: Royal Society of Chemistry51:83, s. 15280-152831359-73451364-548X

Av författaren/redakt...: Klechikov, Alexe ...; Mercier, Guillau ...; Sharifi, Tiva; Baburin, Igor A.; Seifert, Gotthar ...; Talyzin, Alexand ...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.