Radial thermal expansion of single-walled carbon nanotube bundles at low temperatures.

Simultaneous publication in Low Temperature Physics vol. 34, pages 678-679 (2008).
For the first time, the linear coefficient of radial thermal expansion is measured on a system of carbon single-walled nanotube (SWNT) bundles at low temperatures (2.2–120 K). The measurements are performed using a dilatometer with a sensitivity of 2×10−9 cm. A cylindrical sample 7 mm high and 10 mm in diameter was obtained by compressing powder. The resulting bundles of nanotubes are oriented perpendicular to the sample axis. The starting powder consisted of over 90% SWNTs with outer diameter 1.1 nm, the length varying in the range 5–30 µm. A change of sign of the radial thermal expansion coefficient at 5.5 K is observed.

Esel'son, V.B. (författare)
Gavrilko, V. G. (författare)
Manzhelii, V.G. (författare)
Vinnikov, N.A. (författare)
Popov, S.N. (författare)
Sundqvist, BertilUmeå universitet,Institutionen för fysik(Swepub:umu)besu0001 (författare)
Umeå universitetInstitutionen för fysik (creator_code:org_t)

Ingår i:Fizika Nizkikh Temperatur: AIP Publishing34:8, s. 860-8620132-6414
Ingår i:Low Temperature Physics: AIP Publishing34:8, s. 860-8621063-777X1090-6517

Av författaren/redakt...: Dolbin, Alexande ...; Esel'son, V.B.; Gavrilko, V. G.; Manzhelii, V.G.; Vinnikov, N.A.; Popov, S.N.; visa fler...; Sundqvist, Berti ...; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.