Synthesis and high pressure induced amorphization of C60 nanosheets

Selected for Virtual Journal of Nanoscale Science and Technology vol. 16, issue 12 (Sept. 17, 2007).
C-60 nanosheets with thicknesses in the nanometer range were synthesized by a simple method. Compared to bulk C-60, the lattice of the nanosheets is expanded by about 0.4%. In situ Raman spectroscopy and energy-dispersive x-ray diffraction under high pressures have been employed to study the structure of the nanosheets. The studies indicate that the bulk modulus of the C-60 nanosheets is significantly larger than that of bulk C-60. The C-60 cages in nanosheets can persist at pressures over 30 GPa, 3 GPa higher than for bulk C-60. These results suggest that C-60 crystals in even small size will be a potential candidate of superhard materials.

Liu, Bingbing (författare)
Liu, Dedi (författare)
Yao, Mingguang (författare)
Yu, Shidan (författare)
Hou, Yuanyuan (författare)
Zou, Bo (författare)
Cui, Tian (författare)
Zou, Guangtian (författare)
Sundqvist, BertilUmeå universitet,Institutionen för fysik(Swepub:umu)besu0001 (författare)
Luo, Zongju (författare)
Li, Hui (författare)
Li, Yanchun (författare)
Liu, Jing (författare)
Chen, Shijian (författare)
Wang, Guorui (författare)
Liu, Yichun (författare)
Umeå universitetInstitutionen för fysik (creator_code:org_t)

Ingår i:Applied Physics Letters: AIP Publishing91:10, s. 103112-0003-69511077-3118

Av författaren/redakt...: Wang, Lin; Liu, Bingbing; Liu, Dedi; Yao, Mingguang; Yu, Shidan; Hou, Yuanyuan; visa fler...; Zou, Bo; Cui, Tian; Zou, Guangtian; Sundqvist, Berti ...; Luo, Zongju; Li, Hui; Li, Yanchun; Liu, Jing; Chen, Shijian; Wang, Guorui; Liu, Yichun; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.