Pressure effect on electrical properties and photoluminescence spectra of solid C60 and C70 fullerenes

Editors Hans D. Hochheimer, Bogdan Kuchta, Peter K. Dorhout, and Jeffery L. Yarger; invited conference paper
Electrical resistivity of crystalline and disordered fullerite samples obtained by static high-pressure-high-temperature treatment of C-60 and C-70 at P = 12.5 GPa and T = 820-1500 K was investigated in the temperature range of 2.4-300 K, Room-temperature activation energy of charge carriers was found to be in the range 40-200 meV. T-3/2 and T-4 dependencies of conductivity versus temperature were revealed both in crystalline and disordered structures. Photoluminescence spectra of C-60 samples treated at P = 13 GPa. T = 770-1470 K show 50 nm short-wave length shift of characteristic 750 nm PL band.

Blank, Vladimir D. (författare)
Sundqvist, BertilUmeå universitet,Institutionen för fysik(Swepub:umu)besu0001 (författare)
Dubitsky, Gennadii A. (författare)
Prokhorov, V.M. (författare)
Serebryanaya, Nadejda R. (författare)
Kazarian, S.A. (författare)
Oraevsky, A.N. (författare)
Starodubtsev, N.F. (författare)
Umeå universitetInstitutionen för fysik (creator_code:org_t)

Ingår i:Frontiers of High Pressure Research II: Application of High Pressure to Low-Dimensional Novel Electronic MaterialsDordrecht : Springer/Kluwer, s. 483-4919781402001604

Av författaren/redakt...: Buga, Sergei G.; Blank, Vladimir ...; Sundqvist, Berti ...; Dubitsky, Gennad ...; Prokhorov, V.M.; Serebryanaya, Na ...; visa fler...; Kazarian, S.A.; Oraevsky, A.N.; Starodubtsev, N. ...; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.