Solution-Based Phototransformation of C-60 Nanorods : Towards Improved Electronic Devices

• A modified liquid-liquid interface precipitation synthesis of C-60 nanorods, effects and opportunities following an in situ photochemical transformation in the liquid state, and an electronic characterization using a field-effect transistor (FET) geometry are reported. The nanorods feature a high aspect ratio of approximate to 10(3) and a notably small average diameter of 172 nm. Interestingly, it is found that a decreased nanorod diameter appears to correlate with distinctly improved electronic properties, and an average electron mobility of 0.30 cm(2) V-1 s(-1), as measured in a FET geometry, is reported for as-grown nanorods, with the peak value being an impressive 1.0 cm(2) V-1 s(-1). A photoexposure using green laser light ( = 532 nm) is demonstrated to result in the formation of a polymer-C-60 shell encapsulating a monomer-C-60 bulk; such photo-transformed nanorods exhibit an electron mobility of 4.7 x 10(-3) cm(2) V-1 s(-1). It is notable that the utilized FET geometry only probes the polymer-C-60 nanorod surface shell, and that the monomer-C-60 bulk is anticipated to exhibit a higher mobility. Importantly, photoexposed nanorods can be conveniently processed as a stabile dispersion in common hydrophobic solvents, and this finding is attributed to the insoluble character of the polymer-C-60 shell.

Ämnesord

NATURVETENSKAP  -- Kemi -- Fysikalisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Physical Chemistry (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Nanoteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Nano-technology (hsv//eng)

Nyckelord

C-60 nanorods

nanowhiskers

field-effect transistors

liquid-liquid-interface precipitation

photopolymerization

Raman spectroscopy

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)