Influence of water content on hardening and handling of a premixed calcium phosphate cement

• Handling of calcium phosphate cements is difficult, where problems often arise during mixing, transferring tosyringes, and subsequent injection. Via the use of premixed cements the risk of handling complications is reduced. However, for premixed cements to work in a clinical situation the setting time needs to be improved. The objective of this study is to investigate the influence of the addition of water on the properties of premixed cement. Monetite-forming premixed cements with small amounts of added water (less than 6.8 wt.%) were prepared and the influence on injectability, working time, setting time and mechanical strength was evaluated. The results showed that the addition of small amounts of water had significant influence on the properties of the premixed cement. With the addition of just 1.7 wt.% water, the force needed to extrude the cement from a syringe was reduced from 107 (±15)N to 39 (±9)N, the compression strength was almost doubled, and the setting time decreased from 29 (±4)min to 19 (±2)min, while the working time remained 5 to 6 h. This study demonstrates the importance of controlling the water content in premixed cement pastes and how water can be used to improve the properties of premixed cements.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Keramteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Ceramics (hsv//eng)

MEDICIN OCH HÄLSOVETENSKAP  -- Medicinsk bioteknologi -- Biomaterialvetenskap (hsv//swe)

MEDICAL AND HEALTH SCIENCES  -- Medical Biotechnology -- Biomaterials Science (hsv//eng)

Keyword

monetite

brushite

injectability

handling

bone void filler