Crystalline order of polymer nanoparticles over large areas at solid/liquid interfaces

We report on the formation of large two-dimensional domains (about 20 cm2) of oriented and ordered structures of polystyrene particles dispersed in water at a solid/liquid interface. Gentle flow of the dispersed sample into the holder at a shear strain rate of about 0.1 s−1 caused particles at the air/latex meniscus to self-assemble in a regular structure on both solid silica or alumina surfaces. Scattering experiments show that the particle separation at the surface was the same as in the bulk and determined by repulsion arising from the charges on the particles. Close-packed planes formed parallel to the interface.

Kapaklis, VassiliosUppsala universitet,Materialfysik(Swepub:uu)vaska415 (författare)
Rennie, Adrian R.Uppsala universitet,Materialfysik(Swepub:uu)adren227 (författare)
Hughes, Arwel V. (författare)
Porcar, Lionel (författare)
Uppsala universitetMaterialfysik (creator_code:org_t)

Ingår i:Applied Physics Letters: AIP Publishing100:22, s. 221601-0003-69511077-3118

Av författaren/redakt...: Hellsing, Maja S ...; Kapaklis, Vassil ...; Rennie, Adrian R ...; Hughes, Arwel V.; Porcar, Lionel

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.