Frictional behavior of self-adaptive nanostructural Mo-Se-C coatings in different sliding conditions

Artikel/kapitelEngelska2013

Förlag, utgivningsår, omfång ...

Elsevier BV,2013
printrdacarrier

Nummerbeteckningar

LIBRIS-ID:oai:DiVA.org:uu-191179
https://urn.kb.se/resolve?urn=urn:nbn:se:uu:diva-191179URI
https://doi.org/10.1016/j.wear.2013.03.032DOI

Kompletterande språkuppgifter

Språk:engelska
Sammanfattning på:engelska

Ingår i deldatabas

SwePubSwePub

Klassifikation

Ämneskategori:ref swepub-contenttype
Ämneskategori:art swepub-publicationtype

Anmärkningar

Sliding properties of Mo-Se-C coatings with two different carbon content deposited by magnetron sputtering were investigated in different sliding environments (argon, nitrogen, dry and humid air). Both coatings had a structure that was identified as randomly oriented structures of MoSe2 embedded into amorphous carbon matrix. The worn surfaces, i.e. the wear tracks and the wear scars of the balls, were analyzed by optical microscopy, Raman spectroscopy and scanning electron microscopy. The material transferred to the ball steel surfaces was almost exclusively MoSe2, whereas the wear tracks on the coatings were more complex, with areas rich in MoSe2 and areas similar to that of as-deposited coatings. The friction was lowest in argon (0.012 at a load of 10 N) and highest in humid air, but still remarkably low; as best 0.05 at 10 N load; however, the exceptionally low wear rate was almost identical. Thus, we focused our detailed analysis on these two examples to understand the mechanisms responsible for the difference between the friction coefficients. SEM, EDX, XPS, Raman and TEM with EELS and EDX were applied to investigate the composition and structure of localized spots of interest on the tested surfaces. In both cases, we observed well-ordered MoSe2 tribofilms with negligible amount of oxides. Carbon was not present in the sliding interfaces, although large amount of carbon was found outside the contacts on both surfaces. Based on our investigations, we suggest the increase in friction of Mg-Se-C in humid air is primarily due to the increase in shear strength of the MoSe2 structure by the presence of water molecules in the sliding interface

Ämnesord och genrebeteckningar

TEKNIK OCH TEKNOLOGIER Materialteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering hsv//eng
TEKNIK OCH TEKNOLOGIER Nanoteknik hsv//swe
ENGINEERING AND TECHNOLOGY Nano-technology hsv//eng
TEKNIK OCH TEKNOLOGIER Maskinteknik Tribologi hsv//swe
ENGINEERING AND TECHNOLOGY Mechanical Engineering Tribology hsv//eng
Engineering Science with specialization in Materials Science
Teknisk fysik med inriktning mot materialvetenskap

Biuppslag (personer, institutioner, konferenser, titlar ...)

Jacobson, Staffan,1958-Uppsala universitet,Tillämpad materialvetenskap,Tribomaterial(Swepub:uu)stafjaco (författare)
Cavaleiro, Albano (författare)
Polcar, Tomas (författare)
Uppsala universitetTillämpad materialvetenskap (creator_code:org_t)

Sammanhörande titlar

Ingår i:Wear: Elsevier BV303:1-2, s. 286-2960043-16481873-2577

Internetlänk

Hitta via bibliotek

Wear (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

1 av 1
Föregående post
Nästa post
Till träfflistan

Hitta mer i SwePub

Av författaren/redakt...: Gustavsson, Fred ...; Jacobson, Staffa ...; Cavaleiro, Alban ...; Polcar, Tomas

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Nanoteknik

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Maskinteknik; och Tribologi

Artiklar i publikationen: Wear

Av lärosätet: Uppsala universitet

Sök utanför SwePub

Sök vidare i:: Google; Google Book Search; Google Scholar

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

LIBRIS.kb.se