Potential-Induced Degradation of CuIn1-xGaxSe2 Thin Film Solar Cells

Fjällström, ViktorUppsala universitet,Fasta tillståndets elektronik (författare)

The use of Na-free or low Na content glass substrates is observed to enhance the resiliency to potential-induced degradation, as compared with glass substrates with high Na content, such as soda lime glass (SLG). The results from stress tests in this study suggest that degradation caused by a combination of heat and bias across the SLG substrate is linked to increased Na concentration in the CdS and Cu(In,Ga)Se-2 (CIGS) layers in CIGS-based solar cells. The degradation during the bias stress is dramatic. The efficiency drops to close to 0% after 50 h of stressing. On the other hand, cells on Na-free and low Na content substrates exhibited virtually no efficiency degradation. The degraded cells showed partial recovery by resting at room temperature without bias; thus, the degradation is nonpermanent and may be due to Na migration and accumulation rather than chemical reaction.

Salome, P. M. P.Uppsala universitet,Fasta tillståndets elektronik (författare)
Hultqvist, AdamUppsala universitet,Fasta tillståndets elektronik(Swepub:uu)adahu983 (författare)
Edoff, MarikaUppsala universitet,Fasta tillståndets elektronik(Swepub:uu)maribode (författare)
Jarmar, T. (författare)
Aitken, B. G. (författare)
Zhang, K. (författare)
Fuller, K. (författare)
Williams, C. Kosik (författare)
Uppsala universitetFasta tillståndets elektronik (creator_code:org_t)

Av författaren/redakt...: Fjällström, Vikt ...; Salome, P. M. P.; Hultqvist, Adam; Edoff, Marika; Jarmar, T.; Aitken, B. G.; visa fler...; Zhang, K.; Fuller, K.; Williams, C. Kos ...; visa färre...