Lithium storage in amorphous TiNi hydride : Electrode for rechargeable lithium-ion batteries

• In this study, amorphous TiNi phase was successfully prepared using mechanically milling for a very short time of 8 h. HRTEM confirms the formation of amorphous phase with the presence of nanocrystalline Fe particles. After hydrogenation (30 bars of H-2 for a duration of 2 h), the electrochemical reaction shows that TiNi hydride/Li cell discharges at a current of one Li for 10 h between 3 V and 0.005 V. The discharge of TiNiH electrode around x = 1 Li corresponds to a capacity of 251 mAh g(-1) and a hydride composition of TiNiH1.0 at an average voltage of 0.4 V. Ex-situ X-ray diffraction pattern collected at the end of the discharge shows a mixture of amorphous TiNi compound and LiH. A general mechanism for the electrochemical reaction is then proposed: alpha-TiNiH + Li+ + e(-) -> alpha-TiNi + LiH. The results from DFT calculations yield an average cell voltage of 0.396 V, which is in good agreement with the experimental pseudo-plateau occurring at 0.4 V.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Nyckelord

Amorphous materials

Powder metallurgy

Electron microscopy

Powder diffraction

Ab initio calculations

Electrochemical properties

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)