Induced spin-polarization of EuS at room temperature in Ni/EuS multilayers

Ni/EuS multilayers with excellent multilayer sequencing are deposited via e-beam evaporation on the native oxide of Si(100) wafers at 4 x 10(-9) millibars. The samples have very small surface and interface roughness and show sharp interfaces. Ni layers are nanocrystalline 4-8 nm thick and EuS layers are 2-4 nm thick and are either amorphous or nanocrystalline. Unlike for Co/EuS multilayers, all Eu ions are in divalent (ferromagnetic) state. We show a direct antiferromagnetic coupling between EuS and Ni layers. At room temperature, the EuS layers are spin-polarized due to the proximity of Ni. Therefore, Ni/EuS is a candidate for room-temperature spintronics applications. (C) 2014 AIP Publishing LLC.

Goschew, A. (författare)
Kapaklis, VassiliosUppsala universitet,Materialfysik(Swepub:uu)vaska415 (författare)
Wolff, MaxUppsala universitet,Materialfysik(Swepub:uu)maxwo643 (författare)
Delimitis, A. (författare)
Wilhelm, F. (författare)
Rogalev, A. (författare)
Pappas, Spyridon D.Uppsala universitet,Materialfysik(Swepub:uu)spypa516 (författare)
Straub, A. (författare)
Fumagalli, P. (författare)
Uppsala universitetMaterialfysik (creator_code:org_t)

Ingår i:Applied Physics Letters: AIP Publishing104:11, s. 112411-0003-69511077-3118

Av författaren/redakt...: Poulopoulos, P.; Goschew, A.; Kapaklis, Vassil ...; Wolff, Max; Delimitis, A.; Wilhelm, F.; visa fler...; Rogalev, A.; Pappas, Spyridon ...; Straub, A.; Fumagalli, P.; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.