Evolution of CuI/Graphene/Ni(111) System during Vacuum Annealing

We present a combined core-level spectroscopy and low-energy electron diffraction study of the evolution of thin CuI layers on graphene/Ni(111) during annealing. It has been found that the annealing of the CuI/graphene/Ni(111) system up to 160 degrees C results in the formation of an ordered CuI overlayer with a (root 3 x root 3) R30 degrees structure on top of the graphene surface. At annealing temperatures of about 180 degrees C or higher, the CuI overlayer decomposes with a simultaneous intercalation of Cu and I atoms underneath the graphene monolayer on Ni(111). Nearly complete intercalation of graphene by Cu and I atoms can be achieved by deposition of about 20 angstrom of CuI, followed by annealing at 200 degrees C. The intercalated graphene layer is p-doped due to interfacial iodine atoms.

Simonov, Konstantin A.Uppsala University,Lund University,Lunds universitet,Uppsala universitet,Molekyl- och kondenserade materiens fysik,MAX IV-laboratoriet,MAX IV Laboratory,Saint Petersburg State University(Swepub:lu)maxl-kts (författare)
Vinogradov, Nikolay A. (författare)
Zagrebina, Elena M. (författare)
Mårtensson, NilsUppsala universitet,Molekyl- och kondenserade materiens fysik(Swepub:uu)nma32143 (författare)
Preobrajenski, AlexeiLund University,Lunds universitet,MAX IV-laboratoriet,MAX IV Laboratory,Saint Petersburg State University(Swepub:lu)maxl-apr (författare)
Vinogradoy, Alexander S. (författare)
Uppsala universitetMolekyl- och kondenserade materiens fysik (creator_code:org_t)

Ingår i:The Journal of Physical Chemistry C: American Chemical Society (ACS)119:22, s. 12434-124441932-74471932-7455

Av författaren/redakt...: Generaloy, Alexa ...; Simonov, Konstan ...; Vinogradov, Niko ...; Zagrebina, Elena ...; Mårtensson, Nils; Preobrajenski, A ...; visa fler...; Vinogradoy, Alex ...; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.