Naturally Produced Co/CoO Nanocrystalline Magnetic Multilayers : Structure and Inverted Hysteresis

• Cobalt-based multilayers with excellent sequencing are grown via radiofrequency magnetron sputtering with the use of one Co target and natural oxidation. The Co layers are continuous, fully textured {111} and have the face centered cubic structure. At the end of deposition of each Co layer air is let to flow into the vacuum chamber via a fine (leak) valve. The top of Co is oxidized. The oxidized layers consist of cubic CoO crystallites. Near the film surface hexagonal Co(OH)(2) is also detected. Magneto-optical Kerr effect hysteresis loops show in-plane magnetized films. The magnetic saturation field in the out-of-plane measurements is large exceeding 12 kOe. This observation supports indirectly the fact that Co is face centered cubic; if it was c-axis textured hexagonal the magnetocrystalline anisotropy would be large resulting in smaller values of the saturation field. As the Co-layer thickness decreases the in-plane loops show reduced remanence, slow approach to magnetic saturation and the out-of-plane loops show inverted hysteresis and/or crossing loop features with sizeable remanence. The effects are discussed with respect to the enhanced orbital magnetic moment of Co and the antiferromagnetic coupling between Co spins at the Co/CoO interface.

Ämnesord

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Nyckelord

Magnetic Multilayers

Cobalt

Cobalt Oxide

Inverted Hysteresis

Thin Films

Sputtering

Natural Oxidation

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)