Effect of KF absorber treatment on the functionality of different transparent conductive oxide layers in CIGSe solar cells

• This contribution studies the impact of the KF-induced Cu(In,Ga)Se2 (CIGSe) absorber modification on the suitability of different transparent conductive oxide (TCO) layers in solar cells. The TCO material was varied between ZnO:Al (AZO), ZnO:B (BZO), and In2O3:H (IOH). It is shown that the thermal stress needed for optimized TCO properties can establish a transport barrier for charge carriers, which results in severe losses in fill factor (FF) for temperatures >150°C. The FF losses are accompanied by a reduction in open circuit voltage (Voc) that might originate from a decreased apparent doping density (Nd,app) after annealing. Thermally activated redistributions of K and Na in the vicinity of the CdS/(Cu,K)-In-Se interface are suggested to be the reason for the observed degradation in solar cell performance. The highest efficiency was measured for a solar cell where the absorber surface modification was removed and a BZO TCO layer was deposited at a temperature of 165°C. The presented results highlight the importance of well-designed TCO and buffer layer processes for CIGSe solar cells when a KF post deposition treatment (KF-PDT) was applied.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Elektroteknik och elektronik -- Annan elektroteknik och elektronik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Electrical Engineering, Electronic Engineering, Information Engineering -- Other Electrical Engineering, Electronic Engineering, Information Engineering (hsv//eng)

Publication and Content Type

ref (subject category)

art (subject category)